FEATURES • Rutile-Basic stainless steel electrode • Weld on AC or DCEP polarity • Excellent weldability in all position welding except vertical down • Flux coating provides smooth arc transfer and easy slag removal • Designed with low carbon levels to help eliminate carbide precipitation in high temperature service REDRYING • For electrodes that have had a short or mild exposure to the atmosphere, re-drying at 300℃ for 1 hour will be sufficient. For electrodes that have been exposed to longer or more aggressive conditions or critical work environment, re-drying at 300-350℃ for 1-2 hours is recommended. After re-drying, electrodes should be stored in a portable electrode drying oven. APPLICATION • Designed for the welding of 22%Cr-12%Ni base metal and similar alloy composition stainless steels such as ASTM 309 309S 304 305 • Designed for joining stainless steels to mild or low alloy steels • Designed for overlay welding on mild or low alloy steels • Petrol Chemical Industry • Power Generation Construction • Shipbuilding & Offshore