FEATURES • A Rutile-Basic high CrNi-alloyed all position electrode • Weld on AC or DCEP polarity • Flux coating provides Excellent weldability and easy slag removal • Capable of produce duplex weld metal with high crack resistance REDRYING • For electrodes that have had a short or mild exposure to the atmosphere, re-drying at 300℃ for 1 hour will be sufficient. For electrodes that have been exposed to longer or more aggressive conditions or critical work environment, re-drying at 300-350℃ for 1-2 hours is recommended. After re-drying, electrodes should be stored in a portable electrode drying oven. APPLICATION • Designed for the steels difficult to weld such as high C-steels, austenitic Mn- steels, armor steels • Also applied in dissimilar welding joints such as high Ni stainless steel to carbon steel • Welding on cast alloys with similar composition